Waspaloy UNS N07001 W.Nr.2.4654 Ni-Cr-Co Based Superalloy Wire Rod
|
Thông tin chi tiết sản phẩm:
Thanh toán:
|
Chi tiết sản phẩm
| Thành phần hóa học: | Ni-Cr-Co | Ứng dụng: | N07001 |
|---|---|---|---|
| Hình dạng: | gậy | Kích thước: | 1.0mm |
| Màu sắc: | Màu trắng bạc | Tiêu chuẩn: | ASTM,ASTM ASME YB HB BJB GB |
Waspaloy is Ni-Cr-Co based superalloy.Excellent mechanical properties below 980 ° C (1800 ° F), high strength and oxidation resistance at 760-870 ° C (1400-1600 ° F).
Its strength is superior to that of alloy 718 at temperature above 1200-1300℉(650-750℃), and is generally comparable to Haynes R-41 alloy.
Waspaloy Material Composition
| C | Cr | Mo | Ni | Co | Al | Ti | Fe | Si | Mn | P | S | B | Zr | Cu |
| 0.03-0.1 | 18-21 | 3.5-5 | Balance | 12-15 | 1.2-1.6 | 2.75-3.25 | ≤2 | ≤0.15 | ≤0.1 | ≤0.015 | ≤0.015 | 0.003-0.01 | 0.02-0.08 | ≤0.1 |
Waspaloy Material Mechanical Properties
| Grade | Density | Melting Point | Mechanical Property | |||||
| Temperature | Tensile Strength | Yield Strength | Elogation min | Ψ min | Hardness min | |||
| Waspaloy | 8.22 |
1330-1360℃ 2426-2480℉ |
815℃ 1499℉ |
608 Mpa | / | 20 | 32 | 299-387 HBS |
Applications of Waspaloy
Gas Turbine Blades
Sealing Ring
Shaft
Turbine Disc
High Temperature Fasteners
Exotic Fasteners
Special Fasteners
| Alloy Name | Trade Name | UNS NO. | Germany Spec | French Spec | Specification |
| Waspaloy | / | N07001 | W.Nr.2.4654 | NC20K14 |
Waspaloy AMS5708 Waspaloy AMS5709 |
Waspaloy coefficient of thermal expansion
| θ/℃ | 20-100 | 20-200 | 20-300 | 20-400 | 20-500 | 20-600 | 20-700 | 20-800 | 20-900 |
| α | 12.47 | 12.73 | 13.04 | 13.53 | 13.97 | 14.47 | 15.05 | 15.68 | 15.95 |
Waspaloy thermal conductivity
| θ/℃ | 360 | 460 | 545 | 640 | 770 | 855 | 985 |
| W/(m·℃) | 16.8 | 18.3 | 20.2 | 22.4 | 24.1 | 25.3 | 28.0 |
Oxidation resistance in air with a duration of 100h
| θ/℃ | 900 | 1000 |
|
Oxidation rate g/(m2.h) |
0.083 | 0.226 |
Waspaloy welding
Can be fusion welded by argon-arc methods using a matched composition filler metal. If matching alloy is not available, then the nearest alloy richer in the essential chemistry (Ni, Co, Cr, Mo) shall be adopted.
Waspaloy machining
Heavy duty equipment and tooling shall be used to minimize work-hardening of it ahead of cutting.
Chi tiết liên lạc
Ohmalloy Material Co.,Ltd
Người liên hệ: Mr. Qiu
Tel: +8613795230939
Gửi yêu cầu thông tin của bạn trực tiếp cho chúng tôi
Hơn Dây phun nhiệt
-
Sợi nhôm phun nhiệt
-
Dây phun nhiệt Zn85Al15
-
Dây phun nhiệt rắn Ni95Al5 Hiệu suất cao 1.6mm / 2 mm với ISO / CE
-
Phục hồi phần tử máy Monel 400 Dây Chống ăn mòn tốt
-
Nimonic80A. UNS N07080. Hợp kim 80A.2.4952
-
Inconel 625 dây hàn ERNiCrMo-3 với đường kính 1,0 mm cho ứng dụng chống ăn mòn và ổn định nhiệt độ cao